Product introduction
This product is refined from total synthesis isoalkane solvent base oil and total synthesis compound additive.
Characteristics of excellent performance

• Good lubricity for aluminum under the action of fully synthetic additives;
• It has good volatilization performance and very low residual components under heating conditions;
• Good corrosion resistance, especially for aluminum, copper and iron;
• Low friction coefficient and high extreme pressure performance ensure the drawing height of the workpiece in the forming process, at the same time, ensure the abrasive tool and prolong the service life of the mold;
• Light smell, little irritation to skin; High flash point. Made of mineral oil and various additives.

Product use
It is suitable for stamping, punching and drawing of aluminum alloy fins and other metal sheets of air conditioner radiator;  
Main technical specifications

project	Product specification data			test method
	A	B	C
Kinematic viscosity (40℃)mm²/s	1.4	1.65	1.9	GB/T265
density   （15℃）g/cm³	0.7663	0.7847	0.788	GB/T1884
Total acid value,mgKOH/g	0.03	0.04	0.045	ASTM D664
Flash point (closed),℃	70	75	80	GB/T261
Distillation range, ℃ initial boiling point	187	196	199	GB/T6536
Final boiling point	215	238	268
Sulfur content,%（m/m）	0	0	0	GB/T387
Chlorine content,%（m/m）	0	0	0	SH/T0161
Copper corrosion,（100℃×1h），	1	1	1	GB/T5096
Aluminum corrosion,（100℃×３h），	1	1	1	SH/T0195
friction coefficient，（200kgf）	0.04	0.053	0.065	SH/T0190
Maximum no bite load,( PB)	32	33	35	GB/T0202

 matters needing attention

• Water and impurities should be prevented from mixing during storage, transportation and use.
• Don't mix this product with other oil products